Chromes Ores
| Cr2O3 | %38 BASIS %36 MIN. |
| CR/FE RATIO | 2.30/1 MIN. |
| SIO2 | %16 MAX. |
| AL2O3 | %12 MAX. |
| MGO | %24 MAX. |
| P | %0.03MAX. |
| S | %0.03MAX. |
| Size | 0-10 MM %30 MAX. |
| 10-300 MM %70 MIN. |
Chromes Concentrates
| CR2O3 | %48 BASIS %46 MIN. |
| CR/FE RATIO | 2.20/1 MIN. – 2.40/1 MIN. – 2.70/1 MIN. |
| SIO2 | %10 MAX. |
| AL2O3 | %13 MAX. |
| MGO | %23 MAX. |
| P | %0.03 MAX. |
| S | %0.03 MAX. |
| Size | 0-4MM %100 |
Ferro Chromes
| Cr (%) Min. | C (%) Max. | Si (%) Max. | P (%) Max. | S (%) Max. | |
| U-C70Si10 | 65 | 7 | 1 | 0,014 | 0,05 |
| L-C60Si10 | 65 | 6 | 1 | 0,018 | 0,05 |
| L-C80Si15 | 64 | 8 | 1,5 | 0,018 | 0,05 |
| S-C85Si20 | 63 | 8,5 | 2,0 | 0,023 | 0,05 |
| S-C85Si15 | 63 | 8,5 | 1,5 | 0,020 | 0,05 |
| S-C85Si10 | 63 | 8,5 | 1,0 | 0,020 | 0,05 |
| JS-C85Si20 | 62 | 8,5 | 2,0 | 0,020 | 0,05 |
| FS-C85Si25 | 60 | 8,5 | 2,5 | 0,025 | 0,05 |
| Lumpy | 10-50 mm / 10-100 mm / 10-200 mm / +50 mm / +100 mm |
| Fines | 0-3 mm / 0-5 mm / 0-10 mm |
| Tebble | 3-10 mm / 5-10 mm |